Jinan Linquan Industry and Trade Co., Ltd

1)High Temperature Burnt Slide Gate Plate----Mostly for large size slide gate plate----LG21/22 This product adopts tabular alumina, carbonaceous material and zirconia-containing material as main raw materials, adds in high performance antioxidants, uses phenolic resin as binder, formed under high-pressure and burned under high temperature. Mainly used in large and medium-sized ladle. Physical and chemical properties: Al-Zr-C Material Al2O3 C ZrO2 Apparent porosity Bulk density C.C.S (% minm) (% minm) (% minm) (% max) (gm./cc minm) (MPa minm) 85 3 5 7 3.1 120 2) Low Temperature Burnt Slide Gate Plate---Middle size ladles and slide plate Tabular alumina, zirconia-containing material and spinel as major raw materials, adding in special metal, using phenolic resin as binder, being burned under low temperature to produce the products, Mainly used in small and medium-sized ladle. AL-C & AL-Zr-C Al2O3 C ZrO2 Apparent porosity Bulk density C.C.S (% minm) (% minm) (% minm) (% max) (gm./cc minm) (MPa minm) Inner side (Working face) 85 3 4 7 3.1 120 Outside 90 3 0 9 3 3) Unburned Slide Plate ----for small size ladles and slide gate plate No need to be burned, tar impregnated and distilled, simple processing. This product mainly used in small and medium-sized ladle. Physical and chemical properties: Al-C Material Al2O3 C Apparent porosity Bulk density C.C.S (% minm) (% minm) (% max) (gm./cc minm) (MPa minm) 90 3 9 3 120 4. Simple production introduction Our Slide Gate Plate adopts High quality bauxite material , also takes tabular alumina, carbonaceous material and zirconia-containing material as main raw materials, adds in high performance antioxidants, uses phenolic resin as binder, formed under high-pressure and burned under high temperature. The slide plates have the advantages of high strength, good erosion resistance, thermal shock resistance and good stability etc., mainly used in large and medium-sized ladle.