Sino Jincheng Industry Co.,Limited

1) Profile: High Tensile Galvanized Steel Wire or ACSR Core Wire may be supplied as single wire or also in seven strands. Manufactured conforming to various international standards to specify requirement of customers. 2) Application: Used for mechanical re-inforcement in the manufacture of aluminum conductor steel reinforced (ACSR) Cable & Conductor ACSR Core wire is used in reinforcement of aluminium conductors used in distribution and transmission of electricity. 3) Material:  high carbon steel 4) Diameter:  1.25-4.77mm 5) Technical Info:  as below table 6) Packing:  in coils, on spool 7) Standard:  ASTM B498, IEC60888, IS 398 - Part II etc 　 IS BS ASTM IEC ACSR 398 Part II 398 Part V EN 50189 B-498 888 Regular Year 1996 1996 2000 1993 1987 IS 398 - Part II Diameter Tolerance Cross Approx. Breaking load KN* Zn-Coating sectional wt. area 　 Before Minimum Number of CuSO4 5H2O  dipping test 　 　 stranding wt. of coating mm mm mm2 kg/km 　 g/m2 min 1.5 +/-0.03 1.767 13.78 2.46 190 2 1.57 +/-0.03 1.936 15.1 2.7 190 2 1.96 +/-0.04 3.017 23.53 4.2 210 2 2.11 +/-0.04 3.497 27.27 4.6 210 2 2.3 +/-0.05 4.155 32.41 5.46 230 2-½ 2.59 +/-0.05 5.269 41.09 6.92 230 2-½ 3 +/-0.06 7.069 55.13 9.29 240 3 3.18 +/-0.06 7.942 61.95 10.43 250 3 3.35 +/-0.07 8.814 68.75 11.58 250 3 3.53 +/-0.07 9.787 76.34 12.86 250 3 4.09 +/-0.08 13.14 102.48 17.27 275 3-½ * 1 KN = 101.0 kg.   IS 398 - Part V Mechanical Properties Nominal Diameter Size Tolerance Cross Sectional Area Mass Breaking Load Min Zinc Coating No. of 1 Min Cudips mm mm +/- mm2 Kg/km KN Kg/mm2 g/m2 1 min 3.53 0.07 9.787 76.34 12.86 1312 250 3 2.3 0.05 4.155 32.41 5.63 574 230 2-½ 2.54 0.05 5.067 39.52 6.87 700 230 2-½ ASTM B498 - 93 Class A Coating                     ASTM Standard Nominal Diameter (mm) Size Tolerance (mm) Ultimate Tensile Strength Min. Stress at 1 % Extension Min. % Elongation Min. Zn coating Min. Wrapping Mandrel Dia. From To - Incl. + - MPa Kg/mm2 MPa Kg/mm2 GL = 250 mm g/m2 mm 1.27 1.521 0.038 0.025 1450 148 1310 133 3 183 3d 1.524 1.902 0.038 0.025 1450 148 1310 133 3 198 3d 1.905 2.283 0.038 0.025 1450 148 1310 133 3 214 3d 2.286 2.639 0.051 0.051 1410 144 1280 130 3.5 229 4d 2.642 3.045 0.051 0.051 1410 144 1280 130 3.5 244 4d 3.048 3.553 0.076 0.051 1410 144 1240 126 4 259 4d 3.556 4.569 0.102 0.076 1380 141 1170 119 4 274 5d 4.572 4.822 0.102 0.076 1380 141 1170 119 4 305 5d Zn COATING - BS 443 : 1982 Nominal Diameter mm Zn coatng min Number Of Dips min  From - Incl.To g/m2 1 minute 1.24 1.32 170 2 1.32 1.55 180 2 1.55 1.8 200 2 1.8 2.24 215 2 2.24 2.72 230 2-½ 2.72 3.15 240 3 3.15 3.55 250 3 3.55 4.25 260 3 4.25 5 275 3-½ 5 5.5 290 3-½ International Electrotechnical Commission - IEC 888- 1987 - CLASS 1 COATING Regular Grade Nominal Diameter mm Size Tole-rance mm Ultimate Tensile Strength min Stress at 1 % Extension min % Elongation min TORSION Zn Coat- ing min Wrapp- ing Mandrel Dia From To - Incl. +/- N/mm2 Kg/mm2 N/mm2 Kg/mm2 GL=250mm GL=100xd g/m2 (X x OD) 1.24 1.5 0.03 1340 137 1170 119 3 18 185 1 1.5 1.75 0.03 1340 137 1170 119 3 18 200 1 1.75 2.25 0.03 1340 137 1170 119 3 18 215 1 2.25 2.75 0.04 1310 134 1140 116 3 16 230 1 2.75 3 0.05 1310 134 1140 116 3.5 16 230 1 3 3.5 0.05 1290 132 1100 112 3.5 14 245 1 3.5 4.25 0.06 1290 132 1100 112 4 12 260 1 4.25 4.75 0.06 1290 132 1100 112 4 12 275 1 4.75 5.5 0.07 1290 132 1100 112 4 12 290 1 8) All can be produced according to customers’ actual requirement.